Stainless Steel 436 Sheets & SS 436L Sheets
436 stainless steel is a modified version of 434 grade that reduces wrinkling tendency during stringent stretch forming operations. While 430 stainless steel is used for automotive interior trim panels, 434 and 436 grades provide enhanced corrosion resistance for demanding applications.
436 Stainless Steel Specifications
Standard: AISI, ASTM
Model Number: 436
UNS Number: S43600
Chemical Composition
- Carbon (C): ≤ 0.12%
- Manganese (Mn): ≤ 1.00%
- Silicon (Si): ≤ 1.00%
- Chromium (Cr): 16.0-18.0%
- Nickel (Ni): -
- Phosphorus (P): ≤ 0.04%
- Sulfur (S): ≤ 0.03%
- Molybdenum (Mo): 0.75-1.25%
- Niobium (Nb): (5C-0.80)
Mechanical Properties (Annealed Condition)
- Ultimate Tensile Strength: 77 KSI min (531 MPa min)
- Yield Strength (0.2% Offset): 53 KSI min (365 MPa min)
- Elongation: 22% min
- Hardness: HRB 89 max
Available Stainless Steel Products
Grades Available
201, 301, 304, 304L, 309S, 310S, 316L, 317L, 321, 409L, 410, 410S, 430, 439, 444, 904L, 2205, 2507, and more
Surface Finishes
NO.1, 2B, 2D, BA, NO.4, NO.8, 8K, mirror, hair line, sand blast, brush, etching, checkered, embossed, and other specialized finishes
Dimensions
Thickness: 0.2 - 200 mm
Width: 4 - 2000 mm
Length: 500 - 12000 mm / coil
Stainless Steel Composition & Properties
| Grade |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
Hardness |
| 201 |
≤0.15 |
≤1.00 |
5.5/7.5 |
≤0.060 |
≤0.03 |
3.5/5.5 |
16.0/18.0 |
- |
HB≤241,HRB≤100,HV≤240 |
| 304 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.03 |
8.0/11.0 |
18.0/20.0 |
- |
HB≤187,HRB≤90,HV≤200 |
| 316 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.03 |
10.00/14.00 |
16.0/18.0 |
2.00/3.00 |
HB≤187,HRB≤90,HV≤200 |
| 316L |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.045 |
≤0.03 |
10.00/14.00 |
16.0/18.0 |
2.00/3.00 |
HB≤187,HRB≤90,HV≤200 |
| 410 |
≤0.15 |
≤1.00 |
≤1.25 |
≤0.060 |
≤0.03 |
≤0.06 |
11.5/13.5 |
- |
HB≤183,HRB≤88,HV≤200 |
| 430 |
≤0.12 |
≤1.00 |
≤1.25 |
≤0.040 |
≤0.03 |
- |
16.0/18.0 |
- |
HB≤183,HRB≤88,HV≤200 |
Surface Finish Specifications
| Surface |
Feature |
Manufacturing Method |
Application |
| NO.1 |
Silver white matt |
Hot rolled to specified thickness, then annealed and descaled |
Applications not requiring surface gloss |
| NO.2D |
Silver white |
Heat treatment and pickling after cold rolling |
General materials, deep drawing applications |
| NO.2B |
Gloss stronger than NO.2D |
NO.2D treatment with final light cold rolling by polishing rollers |
General materials |
| BA |
Bright as mirror |
Bright annealed surface processing with high reflectivity |
Building materials, kitchen utensils |
| NO.3 |
Rough grinding |
100-200# grinding belt |
Building materials, kitchen utensils |
| NO.4 |
Intermediate grinding |
150-180# abrasive belt polishing |
Building materials, kitchen utensils |
| NO.240 |
Fine grinding |
240# grinding belt |
Kitchenware |
| NO.320 |
Very fine grinding |
320# grinding belt |
Kitchenware |
| NO.400 |
Gloss close to BA |
400# polishing wheel grinding |
General timber, construction, kitchen utensils |
| HL |
Hairline grinding |
150-240# abrasive material with grain texture |
Buildings, construction materials |
| NO.7 |
Close to mirror polishing |
600# rotary polishing wheel |
Art and decoration |
| NO.8 |
Mirror grinding |
Mirror grinding with polishing wheel |
Reflectors, decoration |
Product Applications